1)UHMWPE Pipe/rod Size(mm) |
Max: |
OD-350; L-12000 |
Min: |
OD-7; L-100 |
Standard: |
OD-7/50/60/65/76/89/108/114/127/133/142/159/178/320 |
L-270/350/465/550/750/800/1000/3000/6000/10000 |
UHMWPE Machining |
any size, any sharp, ball, thread or holes are available |
Main Color: |
W/K/B/R/Or/Gr |
Sample Quotation(USD/PC): |
pipe for oil: OD-7,L-10000, Price-1.5 |
|
pipe for roller skin: OD-89,L-200, Price-1.49 |
|
pipe for cement, grain transport: OD-320,L-1000, Price- 49.8 |
Size Tolerance(mm): |
+/-1mm; +/-0.5mm; +/-0.1mm |
Price Term Acceptable: |
EXW; FOB CNSHA; CN main port, CFR |
Payment Term Acceptable: |
30%-50% advance payment |
Packing: |
Bubble wrap , pallet ,steel strip,caton or nonfumigation box |
2)Applictions of UHMWPE Pipe
|
|
1.pipe lining for oil,50mm OD and 3mm thickness |
|
2.lining pipe for Cement, chemical industrial transportation |
|
3.pipe for grain and agricultralal industry |
|
4.UHMWPE Conveyor roller skin |
|
5.Machining for part of plastic,chemical and construction industries. |
|
|
|
3).TFP UHMWPE Material Properties: |
Unit |
Value |
|
Tensile strength(23°C in air) |
Mpa |
>30 |
|
Compression strength |
Mpa |
≥41.8
|
|
Bending strength |
Mpa |
≥32
|
|
Impact strength |
KJ/m² |
≥140
|
|
Ball identation strength |
N/mm² |
≥40.8
|
|
Surface resistivity |
Ω |
4.9×10¹³ |
|
Water absorption |
% |
0.01 |
|
Relative waer rate |
G/cm² |
≤0.09
|
|
Frication coefficent |
% |
<0.09 |
|
Tensile strain at break |
% |
600 |
|
Specific Gravity |
g/cm3 |
0.93-0.96 |
|
Average molecular weight |
g/mol |
3million- 9.8million |
|
Double Notched Impact Strength |
KJ/M2 |
>80 |
|
Brittleness Temp |
°C |
<-70 |
|
Vicat Softing |
°C |
>125 |
|
Heat deflection Temp. |
°C |
>75 |
|
Size Error |
mm |
<0.1 |
|
4). TFP UHMWPE Material Specifications |
|
1.very flat surface. |
|
2.100% pure raw material products, without regrind or recycled material. |
|
3.Thickness 1-100mm, tolerance within 0.1-1mm ,or as required. |
|
4.Color is pure, white, black, red, blue, yellow available. |
|
5.Special shaped pat of UHMW-PE machining work available |
|
6.Special usage, anti-UV, fire-resistant, anti-static UHMW-PE sheet/rod/pipe available. |
|
7.Corrosion resistant, self-lubricating, Lower coefficient of friction, lighter Weight, LONGER life. |
|
|
|
5).TFP UHMWPE Material Advantages |
|
1. high-wear resistance, 7 times as steel, 4 times as PTFE. |
|
2. high-impact resistance, 10 times as PA66, 8 times as PTFE. |
|
3. Splendid self-lubrication, same as PTFE, better than steel/brass appended lubricating oil. |
|
4. Splendid anti-corrosion resistance, resistant to corrosive medium or organic solvent. |
|
5. high-inadhesion resistance, surface can hardly affixe any material. |
|
6. Non-toxic, clean property. |
|
|
|
|
|
|
|